ŽICA BOHLER DMO-IG 2,0x1000

10062
Proizvođač: Voestalpine Böhler
Jedinična cijena: 14,20 € / 1 KG (106.99 HRK)
Cijena pakiranja: 71,00 € (534.95 HRK)
bez PDV-a DOSTUPNO
help_outlinePošaljite upit
ŽICA BOHLER DMO-IG 2,0x1000

ŽICA BOHLER DMO-IG 2,0x1000

Slažem se s Pravilima privatnosti .  

Količina
DOSTUPNO

Minimalna količina narudžbenica za proizvod je 5 kg.

Podaci

Materijal
Čelik
Postupak zavarivanja
TIG - žica
Promjer
2,0

Opis:

2-87
Description
Copper coated GTAW rod for welding in boiler, pressure vessel, pipeline, and crane construction
as well as in structural steel engineering. Very tough deposit of high crack resistant, nonageing.
Recommended for the temperature range from -30 °C to +500 °C. Good copper bonding
with low total copper content. Very good welding and flow characteristics.
Approvals and Certificates
TÜV-D (0020.), KTA 1408.1 (8066.02), DB (42.014.09), ÖBB, TÜV-A (75), BV (UP),
DNV (I YMS), FI (W MoSi), CRS (3), CE
Similar alloy Filler Metals
SMAW electrode: FOX DMO Kb SAW combination: EMS 2 Mo/BB 24
FOX DMO Ti EM2 2 Mo/BB 25
GMAW solid wire: DMO-IG Gas welding rod: DMO
Flux cored wire: DMO Ti-FD
Base Materials
similar alloyed high temperature steels and cast steels, ageing resistant and steels resistant
to caustic cracking
S355J2G3, L290 - L415NB, L290 MB - L415MB, P255G1TH, P235GH, P265GH, P295GH,
P310GH, P255NH, 16Mo3, 17MnMoV6-4, 22NiMoCr4-7, 20MnMoNi5-5, 15NiCuMoNb5S,
20MnMoNi4-5, GE240 - GE300, 22Mo4, S255N - S460N, P255NH - P460NH
ASTM A335 Gr. P1; A161-94 Gr. T1 A A182M Gr. F1; A204M Gr. A, B, C; A250M Gr. T1;
A217 Gr. WC1
Operating Data
shielding gas: 100 % Argon ø mm
1.6
rod marking: 2.0
front: WMoSi 2.4
back: 1.5424 3.0
3.2
Preheating, interpass temperature and post weld heat treatment as required by the base metal.
Mechanical Properties of All-weld Metal
(*) u a
Yield strength Re N/mm2 (MPa): 520 (≥ 480) 480 (≥ 400)
Tensile strength Rm N/mm2 (MPa): 630 (570 - 720) 570 (≥ 520)
Elongation A (L0 = 5d0) %: 27 (≥ 323) 26 (≥ 319)
Impact work ISO-V KV J + 20 °C: 200 (≥ 180) 230 (≥ 200)
- 30 °C: (≥ 347)
(*) u untreated, as-welded – shielding gas Argon
a annealed, 620 °C/1 h/furnace down to 300 °C/air – shielding gas Argon
Typical Composition of Welding Rod
C Si Mn Mo
Wt-% 0.1 0.6 1.2 0.5
EN ISO 21952-A:2008: W MoSi
EN ISO 21952-B:2008: W 52 1M3
EN ISO 636-A:2008: W2Mo (for rod)
EN ISO 636-A:2008: W 46 3 W2Mo
EN ISO 636-B:2008: W 55A 3U W1M3
AWS A5.28-05: ER70S-A1 (ER80S-G)
AWS A5.28M-05: ER49S-A1 (ER55S-G)
W.No.: 1.5424
BÖHLER DMO-IG
GTAW rod, low-alloyed,
high temperature, high strength
High Strength/Cryogenic Filler Metals – GTAW Rods