Materijal
Čelik
Postupak zavarivanja
EPP - žica i prah
Promjer
1,2

Opis:

2-151
Description
The welding consumable Böhler DCMS Ti-FD is a low alloyed, flux-cored wire with rutile filling,
primarily designed for the welding of 1 % Cr and 0,5 % Mo alloyed creep-resistant base metals,
that are used for the fabrication of vessels, high-pressure storage tanks and pipe systems.
Due to the fast freezing slag system this flux-cored wire provides excellent positional welding
characteristics and allows fast travel speeds to be used. This flux cored wire is for welding with
normal power sources on DCRP under Mixture gas (82 % Ar +18 % CO2).
Approvals and Certificates
TÜV-D (11162.), CE
Base Materials
high temperature steels and similar alloyed cast steels, case hardening and nitriding steels of
similar chemical composition, similar alloyed heat treatable steels with tensile strength up to
780 N/mm2, steels resistant to caustic cracking
1.7335 13CrMo4-5, 1.7262 15CrMo5, 1.7728 16CrMoV4, 1.7218 25CrMo4,
1.7258 24CrMo5, 1.7354 G22CrMo5-4, 1.7357 G17CrMo5-5
ASTM A193 Gr. B7; A335 Gr. P11 a. P12; A217 Gr. WC6
Operating Data
re-drying: ø mm amps A
possible, 150 °C / 24 h 1.2 150 - 330
shielding gases:
Argon + 15 - 25 % CO2
Preheating, interpass temperature and post weld heat treatment as required by the base
metal. For heavy walled components an interpass temperature to a min. 175 °C is recommended.
Stress relieved annealing should be carried out between 690 and 710 °C.
Mechanical Properties of All-weld Metal
(*) a
Yield strength Re N/mm2 (MPa): ≥470
Tensile strength Rm N/mm2 (MPa): ≥550
Elongation A (L0 = 5d0) %: ≥ 20
Impact work ISO-V KV J + 20 °C: ≥ 47
(*) a annealed, 690 °C / 1 h – shielding gas Ar + 18 % CO2
Typical Composition of All-weld Metal
C Si Mn Cr Mo P As Sn Sb
Wt-% 0.06 0.22 0.75 1.2 0.47 <0.015 <0.005 <0.005 <0.005
EN ISO 17634-A:2006: (T CrMo1 P M 1)
AWS A5.29-05: E81T1-B2M
AWS A5.29M-05: E551T1-B2M
BÖHLER DCMS Ti-FD
GMAW flux cored wire, low-alloyed,
high temperature
Same Alloy Filler Metals
SMAW electrode: FOX DCMS Kb SAW combination: EMS 2 CrMo/BB 24
FOX DCMS Ti EMS 2 CrMo/BB 25
GTAW rod: DCMS-IG Gas welding rod: DCMS
DCMS-IG B2
GMAW wire: DCMS-IG
High Temperature and Creep-resistant Filler Metals - GMAW Flux cored wires