ŽICA BOHLER FOXCORE 308 L T-1 1.2X15 kg

ŽICA BOHLER FOXCORE 308 L T-1 1.2X15 kg

Slažem se s Pravilima privatnosti .  

Količina
DOSTUPNO

Minimalna količina narudžbenica za proizvod je 15 kg.

Podaci

Materijal
Čelik
Postupak zavarivanja
EPP - žica i prah
Promjer
1,2

Opis:

2-245
Description
Rutile strip alloyed flux cored welding wire with fast freezing slag providing excellent positional operating
characteristics and fast travel speeds. It is easy to use and operates with a powerful penetrating
spray arc transfer, minimum spatter formation and self releasing slag. This flux cored welding wire offers
many economical and quality advantages over solid wire pulse arc welding. High deposition rates and
productivity gains are easily achievable. Additional cost effective benefits are offered through use of less
expensive shielding gases (Argon +15 - 25 % CO2 or 100 % CO2), good wetting characteristics (less
grinding), little temper discoloration & bead oxidation (less pickling expenses), easy operation and safe
penetration (reduces the risk of weld defects and associated repair work costs), and smooth and clean
weld finish (less post weld work). Due to its characteristics mainly for positional welding and service temperatures
between -196 °C to - +350 °C. For downhand & horizontal welding positions (1G, 1F, 2F) our
flux cored wire BÖHLER EAS 2-FD should be preferred.
Approvals and Certificates
TÜV-D (09117.), DB (43.014.23), ÖBB, CWB (E308LT1-1(4)), SEPROZ, GL (4550S (C1,M21))
CE
Same Alloy / Similar Alloy Filler Metals
SMAW electrode: FOX EAS 2 GMAW solid wire: EAS 2-IG (Si)
FOX EAS 2-A Metal cored wire: EAS 2-MC
FOX EAS 2-VD GMAW flux cored wire: EAS 2-FD
GTAW rod: EAS 2-IG EAS 2 PW-FD (LF)
SAW combination: EAS 2-UP/BB202
Base Materials
1.4306 X2CrNi19-11, 1.4301 X5CrNi18-10, 1.4311 X2CrNiN18-10, 1.4312 GX10CrNi18-8,
1.4541 X6CrNiTi18-10, 1.4546 X5CrNiNb18-10, 1.4550 X6CrNiNb18-10
AISI 304, 304L, 304LN, 302, 321, 347; ASTM A157 Gr. C9; A320 Gr. B8C or D
Operating Data
re-drying: ø mm amps A voltage V
possible, 150 °C / 24 h 1.2 100 - 220 20 - 31
shielding gases: 1.6 175 - 260 21 -29
Argon + 15 - 25 % CO2
100 % CO2
Welding with standard GMAW-facilities possible, slightly trailing torch position (angel appr. 80 °), slight
weaving is recommended for positional welding; when using 100 % CO2 as shielding gas it is necessary
to increase the voltage by 2 V; the gas flow should be 15 - 18 l/min
Mechanical Properties of All-weld Metal
(*) u
Yield strength Re N/mm2 (MPa): 380 (≥ 350)
Tensile strength Rm N/mm2 (MPa): 560 (≥ 520)
Elongation A (L0 = 5d0) %: 40 (≥ 335)
Impact work ISO-V KV J +20 °C: 70 (≥ 347)
-196 °C: 40 (≥ 332)
(*) u untreated, as-welded – shielding gas Ar + 18 % CO2
Typical Composition of All-weld Metal
C Si Mn Cr Ni
Wt-% 0.03 0.7 1.5 19.8 10.5
EN ISO 17633-A:2006: T 19 9 L P M 1
T 19 9 L P C 1
EN ISO 17633-B:2006: TS308L-FB1
AWS A5.22-95: E308LT1-4
E308LT1-1
BÖHLER EAS 2 PW-FD
GMAW flux cored wire, high-alloyed,
chemical resistant
Corrosion Resistant Filler Metals – GMAW Flux-cored Wires
www.boehler-welding.com