Žica BOHLER  CN 23/12 Mo-FD  FI 1.2

Žica BOHLER CN 23/12 Mo-FD FI 1.2

Slažem se s Pravilima privatnosti .  

Količina
DOSTUPNO

Minimalna količina narudžbenica za proizvod je 15 kg.

Podaci

Materijal
Čelik
Postupak zavarivanja
EPP - žica i prah
Promjer
1,2

Opis:

2-296
Description
Rutile flux-cored welding wire of type T 23 12 2 L / E309LMoT0 for GMAW of dissimilar joints of Cr- and CrNi(Mo)-
steels and non- or low-alloy steels, as well as weld cladding of un- or low alloyed base metals preferably in flat or horizontal
position. The wire offers a high safety against hot cracking even in the case of high dilution. For Mo-alloyed surfacing
the product is necessary for the 1. layer. This product achieves high productivity and is easy to operate achieving
excellent welding characteristics, self releasing slag, almost no spatter formation and temper discolouration,
smooth weld finish and safe penetration. Beside the major savings in time and cost BÖHLER offers a high production
quality level together with lowest probabilities for welding errors. Increased travel speeds as well as little demand for
cleaning and pickling provide considerable savings in time and money. Suitable for service temperatures of –60 °C to
+300 °C. BÖHLER CN 23/12 Mo-FD ø 0.9 mm is well suitable for welding of sheet metal (thickness greater than 1.5
to 3 mm, for out-of-position welding greater than 5 mm). The slag concept gives the opportunity to weld this diameter
in all welding positions. Wires with ø 1.2 mm can be used for wall thicknesses from 3 mm and up. Wire ø 0,9 mm is
designed for positional welding, wire ø 1.2 mm and 1.6 mm are recommended mainly for downhand and horizontal
welding positions, horizontal/vertical position as well as slightly vertical down position (1 o'clock).
Approvals and Certificates
TÜV-D (5351.), DB (43.014.17), ÖBB, TÜV-A (517), ABS (E 308 MoLT0-4), DNV (309MoL (M21)),
GL (4459 (C1, M21)), LR (X (M21)), RINA (309MO S), SEPROZ, CE
Base Materials
dissimilar joint welds: mild steels and low-alloyed constructional and QT-steels among themselves or among each
other; unalloyed as well as low-alloyed boiler or constructional steels with stainless Cr-, CrNi- and CrNiMo-steels;
ferritic-austenitic joint welds in boiler and pressure vessel parts.
weld surfacing: for the first layer of corrosion resistant surfacing on P235GH, P265GH, S255N, P295GH, S355N
- S500N; for the first layer of corrosion resistant weld surfacing on high temperature quenched and tempered finegrained
steels acc. AD-Merkblatt HPO, class 3.
Typical Composition of All-weld Metal
C Si Mn Cr Ni Mo
Wt-% 0.03 0.6 1.4 23.0 12.5 2.7
EN ISO 17633-A:2006: T 23 12 2 L R M (C) 3
EN ISO 17633-B:2006: TS309LMo-FB0
AWS A5.22-95: E309LMoT0-4 (1)
EN ISO 17633-A:2006: T 23 12 2 L P M (C) 1 (for ø 0.9 mm)
EN ISO 17633-B:2006: TS309LMo-FB1
AWS A5.22-95: E309LMoT1-4/-1 (for ø 0.9 mm)
BÖHLER
CN 23/12 Mo-FD
GMAW flux cored wire,
high-alloyed, special applications
Mechanical Properties of All-weld Metal
(*) u untreated, as-welded – shielding gas Ar + 18 % CO2
Yield strength Re N/mm2 (MPa): 500 (≥ 450)
Tensile strength Rm N/mm2 (MPa): 700 (≥ 550)
Elongation A (L0 = 5d0) %: 30 (≥ 325)
Impact work ISO-V KV J + 20 °C: 55 (≥ 347) - 60 °C: 37 (≥ 332)
Same Alloy/Similar Alloy Filler Metals
SMAW electrode: FOX CN 23/12-A Metal cored wire: CN 23/12-MC
FOX CN 23/12 Mo-A GMAW flux cored wire: CN 23/12-FD
GTAW rod: CN 23/12-IG CN 23/12 PW-FD
GMAW solid wire: CN 23/12-IG CN 23/12 Mo PW-FD
SAW combination: CN 23/12-UP/BB 202
Dissimilar Joints and Special Applications – GMAW Flux-cored Wires
Operating Data
re-drying if necessary: 150 °C/24 h ø mm amps A voltage V
shielding gases: 0.9 100 - 160 21 - 30
Argon + 15 - 25 % CO2 1.2 125 - 280 20 - 34
100 % CO2 1.6 200 - 350 25 - 35
Welding with standard GMAW-facilities possible, slightly trailing torch position
(angel appr. 80 °), when using 100 % CO2 as shielding gas it is necessary
to increase the voltage by 2 V. The gas flow should be 15-18 l/min.
Preheat and interpass temperatures as required by the base metal.
Ø 1.6 Ø 1.2 Ø 0.9