Elektroda Bohler  Fox Cm 5 Kb fi 3,2

Elektroda Bohler Fox Cm 5 Kb fi 3,2

Slažem se s Pravilima privatnosti .  

Količina
DOSTUPNO

Minimalna količina narudžbenica za proizvod je 4,2 kg.

Podaci

Materijal
Inox
Postupak zavarivanja
REL - elektroda
Promjer
3,2

Opis:

2-117
Description
Basic core wire alloyed electrode for high temperature steels and steels for hot hydrogen service.
Preferably used for X12CrMo5 (5 Cr 0.5 Mo) steels. Approved in long-term condition up to
+650 °C service temperature.
High crack resistance, very low hydrogen content (acc. AWS condition HD < 4 ml/100 g). Good
weldability in all positions except vertical down. The deposit is heat treatable. Metal recovery
approx. 115 %.
Approvals and Certificates
TÜV-D (0725.), TÜV-A (695), LTSS, VUZ, SEPROZ, CE
Same Alloy Filler Metals
GTAW rod: CM 5-lG
GMAW solid wire: CM 5-lG
SAW combination: CM 5-UP/BB 24
Base Materials
high temperature steels and similar alloyed cast steels, QT-steels similar alloyed up to
1180 N/mm2 tensile strength.
1.7362 X12CrMo5, 1.7363 GX12CrMo5
ASTM A213 Gr. T5; A217 Gr. C5; A335 Gr. P5
Operating Data
re-drying if necessary: ø mm L mm amps A
300 - 350 °C, min. 2 h 2.5 250 70 - 190
electrode identification: 3.2 350 110 - 130
FOX CM 5 Kb 8018-B6 E CrMo 5 B 4.0 350 140 - 170
Preheat and interpass temperatures 300-350 °C. Post weld annealing at 730-760 °C for at least
1 hour followed by cooling in furnace down to 300 °C and still air.
Mechanical Properties of All-weld Metal
(*) a v a2
Yield strength Re N/mm2 (MPa): 520 (≥ 420) 440 (≥ 390) (≥ 460)
Tensile strength Rm N/mm2 (MPa): 620 (≥ 590) 580 (≥ 570) (≥ 550)
Elongation A (L0 = 5d0) %: 21 (≥ 318) 26 (≥ 318) (≥ 319)
Impact work ISO-V KV J + 20 °C: 90 (≥ 380) 110 (≥ 380)
(*) a annealed 730 °C/2 h/furnace down to 300 °C/air
a2 annealed, 760 °C/1 h/furnace down to 200 °C/air
v quenched/tempered, 960 °C/0.5 h/oil + 730 °C/0.5 h/furnace down to 300 °C/air
Typical Composition of All-weld Metal
C Si Mn Cr Mo
Wt-% 0.08 0.3 0.8 5.0 0.6
EN ISO 3580-A:2008: E CrMo5 B 4 2 H5
EN ISO 3580-B:2008: E5518-5CM H5
AWS A5.5-06: E8018-B6H4R
AWS A5.5M-06: E5518-B6H4R
BÖHLER FOX CM 5 Kb
SMAW basic electrode, low-alloyed,
high temperature
High Temperature and Creep-resistant Filler Metals – SMAW Covered Electrodes
www.boehler-welding.com