ELEKTRODA BOHLER FOX EAS 2-A FI 3,2

9630
Proizvođač: Voestalpine Böhler
Jedinična cijena: 36,08 € / 1 KG (271.84 HRK)
Cijena pakiranja: 147,93 € (1114.58 HRK)
bez PDV-a DOSTUPNO
help_outlinePošaljite upit
ELEKTRODA BOHLER FOX EAS 2-A FI 3,2

ELEKTRODA BOHLER FOX EAS 2-A FI 3,2

Slažem se s Pravilima privatnosti .  

Količina
DOSTUPNO

Minimalna količina narudžbenica za proizvod je 4,1 kg.

Podaci

Materijal
Inox
Postupak zavarivanja
REL - elektroda
Promjer
3,2

Opis:

2-186
Description
Rutile electrode, core wire alloyed, stainless steel. Preferably used for 1.4306 / 304L / 304LN
steel grades.
BÖHLER FOX EAS 2-A is noted for its superior welding characteristics and metallurgy. Can be
used on AC or DC. Other characteristics include high current carrying capacity, minimum
spatter formation, self releasing slag, smooth and clean weld profile, safety against formation
of porosity due to moisture resistant coating and packaging into hermetically sealed tins.
Resistant to intergranular corrosion up to +350 °C.
Approvals and Certificates
TÜV-D (1095.), DB (30.014.15), ÖBB, TÜV-A (96), ABS (E 308L-17), GL (4306), Statoil, VUZ,
SEPROZ, CE
Same Alloy/Similar Alloy Filler Metals
SMAW electrode: FOX EAS 2 Metal cored wire: EAS 2-MC
FOX EAS 2-VD Flux cored wire: EAS 2-FD
GTAW rod: EAS 2-IG EAS 2 PW-FD
GMAW solid wire: EAS 2-IG (Si) EAS 2 PW-FD (LF)
SAW combination: EAS 2-UP/BB 202
Base Materials
1.4306 X2CrNi19-11, 1.4301 X5CrNi18-10, 1.4311 X2CrNiN18-10, 1.4312 GX10CrNi18-8,
1.4541 X6CrNiTi18-10, 1.4546 X5CrNiNb18-10, 1.4550 X6CrNiNb18-10
AISI 304, 304L, 304LN, 302, 321, 347; ASTM A157 Gr. C9; A320 Gr. B8C or D
Operating Data
re-drying if necessary: ø mm L mm amps A
120 - 200 °C, min. 2 h 1.5 250 25 - 140
electrode identification: 2.0 300 40 - 160
FOX EAS 2-A 308L-17 E 19 9 L R 2.5 250/350 50 - 190
3.2 350 80 - 120
4.0 350 110 - 160
5.0 450 140 - 200
Mechanical Properties of All-weld Metal
(*) u sa
Yield strength Re N/mm2 (MPa): 430 (≥ 350)
Tensile strength Rm N/mm2 (MPa): 560 (≥ 520)
Elongation A (L0 = 5d0) %: 40 (≥ 335)
Impact work ISO-V KV J + 20 °C: 70 (≥ 347)
- 120 °C: (≥ 332)
- 196 °C: (≥ 332)
(*) u untreated, as-welded
sa solution annealed and quenched
Typical Composition of All-weld Metal
C Si Mn Cr Ni
Wt-% 0.03 0.8 0.8 19.8 10.2
EN 1600:1997:E 19 9 L R 3 2
AWS A5.4-06: E308L-17 BÖHLER FOX EAS 2-A
SMAW rutile electrode, high-alloyed,
chemical resistant
Corrosion Resistant Filler Metals – SMAW Covered Electrodes
www.boehler-welding.com